Takze pravda je asi tato:
************************************************************************
Thermal cure:
For easily etched material in typical acidic or ammoniacal etchants no
additional curing is required. Anyhow for etching of difficult to etch
materials (steel or steel alloys) requiring long etching times, an
additional thermal cure after developing is recommended. This also
applies for subsequent plating processes in critical plating baths.
Normally a thermal cure of 10 to 30 minutes at 120°C is sufficient, but
for difficult to etch metals a thermal cure at 160 to 190 °C is
suggested. Very hot cured coats can only be removed mechanically
(scourers, brushes).
************************************************************************
--
Jirka
Danhard napsal(a):
> Odecti ty 2 stupne na zacatku, a bude to spravne 70, chyba byla jenom 2 stupne
> Celsia :o))
>
> Danhard
> ------------
>
>
> Marek napsal(a):
>
>
>>No ja hodlam poexperimentovat s POSITIV20. Nekde ve
>>specifikaci jsem nasel info, ze v pripade vytvrzeni ve
>>vyzsich teplotach odolava rozpoustedlum a (doufam) by mohla
>>vydrzet i teplotu pajeni. Odstraneni pry je mozne jen
>>obrousenim... Chtel jsem s tim experimentovat (ale treba uz
>>nekdo ma zkusenosti). Neco jako: vyrobim plosnak (vcetne
>>odleptani) -> nenesu POSITIV20 -> osvetlim -> vyvojka ->
>>vytvrzeni pri 270 (tato teplota tam byla udavana). Pokud to
>>nekdo zkusi driv jak ja - prosil bych o info.
>
>
> Pokud me smysly, zkusenost a dalsi drobnosti neklamou: jestlize
> vystavite normalni cuprextit po _delsi dobu_ (ktera je nepochybne nutna
> k vytvrzeni toho Positivu) teplote 270 stupnu, tak uz to nebude cuprextit...
>
> Clovece, zkuste trochu myslet, pojivem laminatu je vcelku bezny epoxid
> nebo polyester. Nepredpokladam, ze budete pouzivat teflonovy nebo
> keramicky substrat.
>
> --